UV-induced degradation of PERC solar modules with UV-transparent encapsulation materials
- verfasst von
- Robert Witteck, Boris Veith-Wolf, Henning Schulte-Huxel, Arnaud Morlier, Malte R. Vogt, Marc Köntges, Rolf Brendel
- Abstract
In this paper, we report on the stability of p-type passivated emitter and rear cells under ultraviolet (UV) exposure with various silicone nitride passivation coatings and embedded in different encapsulation polymers. Our results reveal that UV transparent polymers can result in a module power loss of up to 6% under a UV irradiation dose of 497 kWh/m2. We show that the degradation in power is caused by a reduction in open circuit voltage. This loss is related to an increased recombination in the cell, which we ascribe to a degradation of the surface passivation. With ray tracing simulations, we determine the number of photons reaching the passivation interface. Assuming that all photons with energies above 3.5 eV de-passivate the interface is in agreement with our experimental results.
- Organisationseinheit(en)
-
Abt. Solarenergie
- Externe Organisation(en)
-
Institut für Solarenergieforschung GmbH (ISFH)
- Typ
- Artikel
- Journal
- Progress in Photovoltaics: Research and Applications
- Band
- 25
- Seiten
- 409-416
- Anzahl der Seiten
- 8
- ISSN
- 1062-7995
- Publikationsdatum
- 06.2017
- Publikationsstatus
- Veröffentlicht
- Peer-reviewed
- Ja
- ASJC Scopus Sachgebiete
- Elektronische, optische und magnetische Materialien, Erneuerbare Energien, Nachhaltigkeit und Umwelt, Physik der kondensierten Materie, Elektrotechnik und Elektronik
- Ziele für nachhaltige Entwicklung
- SDG 7 – Erschwingliche und saubere Energie
- Elektronische Version(en)
-
https://doi.org/10.1002/pip.2861 (Zugang:
Geschlossen)