Impact of hydrogen on the permanent deactivation of the boron-oxygen-related recombination center in crystalline silicon

verfasst von

Dominic Walter, Jan Schmidt

Abstract

In a series of lifetime experiments, we examine the impact of hydrogen on the permanent deactivation of the boron-oxygen (BO)-related defect center in Czochralski-grown boron-doped silicon. In the first experiment, the hydrogen concentration in the external source is varied by the deposition of dielectric layers containing various hydrogen concentrations (aluminum oxide and silicon nitride layers) before applying a fast-firing step at high temperature (>800 °C). In the second experiment, the sample cooling rate after high-temperature treatment is varied without hydrogen-rich dielectric layer being present and the surface passivation based on aluminum oxide is applied at low temperature afterwards. In both experiments, it is observed that the sample cooling after the high-temperature treatment has the major impact on the dynamics of BO deactivation process and fast cooling rates enable a fast deactivation. No direct impact of the hydrogen content in the dielectric layers being present during the fast-firing step on the dynamics of the BO deactivation is observed. However, the highest lifetimes in excess of 1 ms are only achievable when a hydrogenation step is performed, which we interpret in terms of a hydrogen passivation of background defects of hitherto unknown nature. In a third experiment, we apply an organic passivation layer by spin-coating, which is dried at low temperature (130 °C). We find in this experiment that even without any hydrogen intentionally introduced into the silicon bulk, an effective deactivation of the BO center can be observed, clearly supporting that no hydrogen is required to enable the BO deactivation.

Organisationseinheit(en)

Institut für Festkörperphysik

Externe Organisation(en)

Institut für Solarenergieforschung GmbH (ISFH)

Typ

Artikel

Journal

Solar Energy Materials and Solar Cells

Band

158

Seiten

91-97

Anzahl der Seiten

7

ISSN

0927-0248

Publikationsdatum

12.2016

Publikationsstatus

Veröffentlicht

Peer-reviewed

Ja

ASJC Scopus Sachgebiete

Elektronische, optische und magnetische Materialien, Erneuerbare Energien, Nachhaltigkeit und Umwelt, Oberflächen, Beschichtungen und Folien

Ziele für nachhaltige Entwicklung

SDG 7 – Erschwingliche und saubere Energie

Elektronische Version(en)

https://doi.org/10.1016/j.solmat.2016.05.025 (Zugang: Geschlossen)